Atomistic Study of Interactions between Intrinsic Kink Defects and Dislocations in Twin Boundaries of Nanotwinned Copper during Nanoindentation

Abstract

In order to study the effects of kink-like defects in twin boundaries on deformation mechanisms and interaction between dislocations and defects in twin boundaries under localized load, nanotwinned Cu with two defective twin (TDT) boundaries is compared with the nanotwinned Cu with two perfect twin (TPT) boundaries, and nanotwinned Cu with single defective twin (SDT) boundary and single perfect twin boundary by simulating spherical nanoindentations using molecular mechanics. The indenter force-depth and hardness-contact strain responses were analyzed. Results show that the existence of intrinsic defects in twin boundary could reduce the critical load and critical hardness of nanotwinned material. A quantitative parameter was first proposed to evaluate the degree of surface atom accumulation around the indenter during nanoindentation, and it can be inferred that the surface morphology in TDT changes more frequently than the surface morphologies in TPT and SDT. The atomistic configurations of incipient plastic structures of three different models were also analyzed. We found that the intrinsic defects in twin boundary will affect the incipient plastic structures. The formation of twinning partial slip on the defective twin boundary happens before the contact of the dislocation and twin boundary. The kink-like defects could introduce Frank partial dislocation to the twin boundary during interaction between dislocation and twin boundary, which was not detected on the perfect twin boundary. In addition, the area of twinning partial slips on the upper twin boundary in the incipient plastic structures in SDT and TDT are larger than the twinning partial slip area in TPT, which results in the reduction of the critical hardness in SDT and TDT. The kink-like defects could also block the expansion of twinning partial slip on the twin boundary. Furthermore, we investigated the dislocation transmission processes in three different models. It is found that the dislocation transmission event could be delayed in model containing single defective twin boundary, while the transmission process could be advanced in model containing two consecutive defective twin boundaries.